英文原题：LPEO enhanced LAGP composite solid electrolytes for lithium metal batteries
作者：Dongmei Dai, Pengyao Yan, Xinxin Zhou, Haowen Li, Zhuangzhuang Zhang, Liang Wang, Mingming Han, Xiaobing Lai, Yaru Qiao, Mengmin Jia*, Bao Li*, Dai-Huo Liu*
01
背景介绍
Background
商业锂离子电池通常使用有机溶剂作为电解液，其易燃特性将带来安全性问题，同时锂枝晶生长的问题也颇为棘手。固态电解质，包括聚合物固态电解质与无机固态电解质，被认为是解决上述问题的有效举措。其中，NASICON型无机固态电解质Li1+xAlxGe2–x(PO4)3（LAGP）具有高的室温电导率、宽的电化学窗口和优异的空气环境稳定性，是最有望实现大规模产业化的固态电解质之一。然而NASICON型LAGP与锂金属间的界面兼容性较差，导致界面阻抗较大和差的循环稳定性。
河南师范大学化学化工学院的李苞教授、刘代伙副教授等于Green Carbon上发表标题为“LPEO enhanced LAGP composite solid electrolytes for lithium metal batteries”的研究文章，研究了LPEO界面修饰层的提升机理，揭示了LPEO层对提升金属锂负极与LAGP界面兼容性、稳定性、离子传输、以及电池长期稳定循环的重要性。
1
1
02
文章简介
Introduction
提升界面兼容性
1
1
如图1a和1b所示，成功制备了无机固态电解质LAGP粉末。利用LPEO改善LAGP表界面（图1c），相较于粗糙和不平整的LAGP（图1d-e），经过LPEO界面修饰的LAGP表面变得更平整和致密（图1f-g所示），有利于提升与锂负极的界面兼容性和亲密接触性，降低界面间的阻抗和改善锂离子传输动力学。
图1. LPEO对LAGP固态电解质的界面修饰
1
提升锂离子的界面传输和稳定性
1
1
如图2a和2b所示，对LPEO的剂量和浓度进行优化，电化学性能表明其最优参数分别为20 μL和0.095 g mL-1。电池的变温阻抗及其阿伦尼乌斯拟合计算了离子传输的活化能，结果如图2c和2d所示。利用LPEO修饰的LAGP其室温离子电导率约为8.22×10-4 S cm-1，可较好的满足电池在室温下工作的要求，其活化能约为0.15 eV，说明LAGP是一种良好的离子导体，有利于Li+的快速迁移。其中，PEO链中（CH2-CH2-O）嵌段的摆动也能促进Li+的迁移。此外，LAGP电解质两侧的LPEO修饰层能增强其与锂负极的界面相容性和降低界面阻抗。
图2. LPEO剂量参数的优化及其界面离子传输性能改性测试
锂金属负极与LAGP界面稳定性表征
1
1
如图3a所示，采用不同界面修饰的LAGP组装对称电池并测试其循环性能和界面性质。结果表明，采用LEPO作为界面修饰层的对称电池可实现稳定循环600 h且保持较小的电化学极化，而采用普通商业电解液和未进行界面修饰的对称电池均表现出较大的极化和短的循环寿命。因此，LPEO作为界面缓冲层，不仅可以起到润湿界面的作用，避免LAGP与锂金属的副反应，还可以调节Li+流的均匀性，抑制锂枝晶的生长。临界电流密度结果表明，用LPEO-LAGP组装的对称电池具有更好的循环可逆性(图3b)。如图3c所示，含LPEO-LAGP的对称电池具有最小的界面阻抗，表明其能够加快离子的界面传输能力，提升电池的倍率性能。循环后的界面形貌表征结果如图3d-e所示，采用LPEO-LAGP的对称电池循环之后界面较光滑和平整，采用LE-LAGP的对称电池循环后表面较粗糙，表明了对LAGP进行了界面修饰的重要性。同时，对循环后的LAGP固态电解质界面进行XPS表征（图3f）。采用LE的对称电池循环后LAGP中的Ge4+被还原为+2和0价，而采用LPEO的LAGP的+4价Ge4+未被还原，表明LPEO作为界面缓冲层抑制了金属锂和LAGP的副反应，提升了LAGP的界面稳定性。
图3. LPEO对金属锂负极的界面稳定提升机制
界面改善提升锂金属电池的循环稳定性
1
LPEO层的引入提高了固态电解质/锂负极界面间的兼容性和电化学循环稳定性。图4a和4b分别为锂/LFP全电池从0.1 C到2 C下的倍率性能和对应的电压-容量曲线，在较低的倍率下，含LPEO-LAGP和LE-LAGP的电池表现出相近的极化。然而，随着倍率的逐渐增加，LE-LAGP的极化急剧上升，而采用LPEO-LAGP的极化电压变化不大，这表明添加LPEO的LAGP固态电池具有更好的界面浸润性和较好的离子传输行为。图4c可以看出，在0.4 C（室温）条件下，含LPEO-LAGP的全电池的初始容量为158 mAh g-1，高于LE-LAGP全电池的120 mAh g-1，而在138 次循环后，使用LE作为改性剂的全电池的容量因严重的副反应而急剧下降，而采用LPEO为改性剂的电池在循环200次后，容量保持率仍有74%。综上所述，LPEO作为界面修饰层可极大地增强界面浸润性和稳定性、抑制LAGP的界面副反应、加速离子的界面迁移动力学，从而改善固态锂金属电池的长期循环稳定性和实现优异的室温性能。
图4. LPEO改性的固态锂金属电池的倍率性能和循环性能
总结及展望
1
总之，利用LPEO作为界面缓冲层，解决了LAGP与锂负极界面间的界面兼容性、离子传输动力学、界面副反应、大的界面阻抗等界面问题。在0.1 mA cm-2下，含LPEO的Li/Li对称电池可连续工作600小时。更重要的是，Li/LPEO-LAGP/LFP全电池表现出了更优越的倍率和循环性能。此外，在2.8-4.3 V的电压窗口下，Li/LPEO-LAGP/NCM811全电池在0.2 C下循环100次仍可获得高的比容量140 mAh g-1。
03
文章摘要
Abstract
1
Abstract
The application of solid electrolyte is expected to realize the commercialization of high energy density lithium metal batteries (LMBs). While the interfacial contact between solid inorganic electrolyte and electrodes has become a stumbling block for achieving stable cycling in LMBs. In this work, a Li-containing polyethylene oxide (LPEO) was introduced between LAGP and electrodes as a buffer layer to regulate the interfacial compatibility and reduce interfacial impedance, inhibiting the side reactions. Moreover, ether-oxygen bond on LPEO chain can coordinate with Li+ and guide the transportation of Li+, achieving fast Li+ diffusion between Li1+xAlxGe2-x(PO4)3 (LAGP) and electrodes. Specifically, the growth of lithium dendrites is effectively suppressed in LAGP with LPEO modification, which would lead to remarkable cycling stability and rate capability. Therefore, the Li|LPEO-LAGP|Li battery can cycle stably for more than 600 h at 0.1 mA cm−2. In addition, long-term performance of Li|LPEO-LAGP| LiFePO4 (LFP) battery was achieved at a rate of 0.4 C, and capacity retention is more than 74% after 200 cycles. The Li|LPEO-LAGP|LiNi0.8Co0.1Mn0.1O2 also realized the steady operation in the voltage range of 2.8–4.3 V.
04
作者
Author
李苞 教授
李苞，博士，河南师范大学化学化工学院教授。现担任河南师范大学科技处副处长，研究方向是新型电池隔膜/固态电解质的开发与改性，主持国家自然科学基金项目2项、省科技厅、教育厅重点项目。已发表SCI论文30余篇，授权专利5项。获得河南省文明教师、省一流课程负责人。
刘代伙 副教授
05
相关论文信息
Information
本文为开放获取文章
扫描二维码或点击左下角“阅读全文”可查阅全文
论文信息
D. Dai, P. Yan, X. Zhou, et al. LPEO enhanced LAGP composite solid electrolytes for lithium metal batteries[J]. Green Carbon, 2024.
论文网址
https://doi.org/10.1016/j.greenca.2024.06.002
论文下载
LPEO enhanced LAGP composite solid electrolytes for lithium metal batteries.pdf
供稿：贾梦敏 副教授
（河南师范大学）
编辑：Green Carbon 期刊中心
审核：Green Carbon 期刊中心
//////////
Green Carbon
关于
Green Carbon
1
Green Carbon（绿碳，ISSN 2950-1555）是由中国科学院青岛生物能源与过程研究所创办、与科爱集团联合出版的开放获取英文学术期刊，聚焦绿色碳资源的开发与利用、化石碳资源的绿色转化与利用、排放碳资源的固定与利用，以及多尺度碳循环的分析与管理等主题，推动可持续发展领域的科技创新，打造多学科融合的国际一流学术交流平台。期刊将发表原创性研究论文、综述类文章、社论、简短通讯、观点和专题类文章。
中国科技期刊卓越行动计划高起点新刊 CAS数据库收录 2025年底前稿件处理费用（APC）由编辑部承担，作者无需支付任何费用 对已接收文章免费进行语言润色服务 黄金开放获取期刊，已出版论文可以免费全文下载 https://www.sciencedirect.com/journal/green-carbon
优秀文章提供免费精准推送服务
官方网站
https://www.keaipublishing.com/en/journals/green-carbon/
联系方式
greencarbon@qibebt.ac.cn
欢迎访问期刊主页
扫码进入文章投稿
编辑部联系方式
邱翔 博士
电话：（0532）58261072；15640526517
邮箱：qiuxiang@qibebt.ac.cn；
greencarbon@qibebt.ac.cn
路帅敏 博士
电话：（0532）58261072；13210205278
邮箱：lusm@qibebt.ac.cn；
greencarbon@qibebt.ac.cn
地址：山东省青岛市崂山区松岭路189号，266101
长按关注
欢迎您的投稿！
往期目录
1卷1期
1卷2期
2卷1期
2卷2期
经典回顾